DESCRIPTION
Rhino/CoverCat 406™ has excellent heat resistance properties allowing its use in elevated temperature environments. It also superior adhesion to damp substrates such as iron, steel, clay, and cementitious pipe or similar conveyances requiring coating and rehabilitation.
Applications are tack free within 2-3 hours and may be immediately recoated to achieve additional coats of up to 20 mils to repair cracks or fill defects. Pipes lined with the Rhino/CoverCat 406 are returned to service within 24 hours, and will cure underwater providing an exceptionally fast pipe placement and service turnaround. Rhino/CoverCat 406 meets NSF 61 standards and fulfills other demanding and time critical application requirements.
FEATURES & BENEFITS
- Rapid installation of semi structural high build pipe linings and coatings
- 24 hour return to service for potable water pipe lining to NSF standard 61
- Extremely tolerant of damp or humid environments, will cure underwater
- Monolithic repair membrane that bridges small cracks and other defects
- Chemical resistant for gas, oil and other industrial processing applications
- Heat resistant to 175°F (80°C); suited to hot water pipes / elevated temperature environments
- Excellent adhesion to damp, cool substrate
- Available in Blue, Green, or Natural color(s)
| • Coverage Rate @ 20 mils (500 microns): | 80 sq ft/gallon (2 sq meters/liter) |
| • % Solids by Weight: | 100% |
| • Specific Gravity: | 1.45 |
| • Mixed Viscosity: | Highly thixotropic sprayable paste |
| • Working Time: | 15-20 minutes |
| • Tack Free Time: | 2-3 hours |
| • Return to Service: | 24 hours |
| • Speed of Application: | >600 meters/shift (depending on pipe diameter) |
| • Compressive Strength (psi) ASTM D695: | 12,000 – 14,000 |
| • Flexural Strength (psi) ASTM D790: | 13,000 – 13,800 |
| • Tensile Strength (psi) ASTM D638: | 7,000 – 8,000 |
| • Tensile Elongation (%) ASTM D638: | 4.50% |
| • HDT, ASTM D648-264: | 175°F (80°C) |
| Chemical | % Weight Gain (Loss) |
| Xylene | 0.0 |
| Toluene | 2.3 |
| Trichloroethane | 0.0 |
| MEK | 2.3 |
| 10% Sulfuric Acid | 0.0 |
| 70% Sulfuric Acid | .02 |
| 10% Hydrochloric Acid | .01 |
| 50% Sodium Hydroxide | (.02) |
| Skydrol | (.03) |
| Mogas, Diesel | 0.0 |
| JP-4, JP-5, JP-7, JP-8 | 0.0 |