DESCRIPTION

Novel modified cycloaliphatic hardener. High strength, low viscosity curing agent with fast thin film set time, rapid oven cure and high HDT after post cure. Cures sufficiently at ambient temperatures for unsupported post cure. Contains no solvents, 100% solids.

SUGGESTED USES

Novel modified cycloaliphatic hardener. High strength, low viscosity curing agent with fast thin film set time, rapid oven cure and high HDT after post cure. Cures sufficiently at ambient temperatures for unsupported post cure. Contains no solvents, 100% solids.
 
Viscosity at 77°F cps: 50-70 cps
Mixed Viscosity with 1403 Resin: 300-400 cps
Mixed Viscosity with 1403T Resin: 1300-1400 cps
Color (Gardener): 2 max
Weight Per Gallon: 8.2 lbs
Mix Ratio, Parts Per 100 of Resin: 20 by weight (100: 12 when used with 908SC)
Gel Time at 77°F (150 grams) 25-30 minutes
Thin Film Set Time, Hours 2
 
(Cure schedule: 24 hrs at ambient + 2 hrs at 100°C + 2 hrs at 150°C
DHT, °F >300 (>250 after 7 days at ambient)
Shore D Hardness 90 + 5
Flexural Strength, psi 19,000
Flexural Modulus, psi 495,000
Tensile Strength, psi 11,500
Tensile Modulus, psi 522,000
Elongation % 3.5

 

FOB Rhino Linings, San Diego or authorized distributors. Rhino 3136R-1: 8lb Gallons, 40lb Pails and 450lb Drums.
0
CURE TIME (SECONDS)
0
RHINO EMPLOYEES
0
COUNTRIES SERVED
0%
CUSTOMER SATISFACTION

APPLICATION PROCESS

CREATING ART WITH RHINO

SPRAY FOAM ROOFING

EPOXY FLOOR COATING

Find out how our product solutions can help expand your business: 800-422-2603