DESCRIPTION

Rhino 1310T epoxy composites are non-draining, 100% solids systems that provide maximum flexibility for a variety of reinforced composites. Whether performing fiberglass infrastructure reinforcement, seismic retrofits, or the repair of failing conventional concrete/rebar structures, Rhino 1310T forms a matrix in which carbon or glass fiber is saturated then woven together to add structural reinforcement.

Rhino fiberglass infrastructure reinforcement and seismic retrofits last longer and incur a fraction of the cost and time it takes to achieve the same results using conventional materials and techniques. Carbon fiber wrap and blast mitigation solutions are currently being used in numerous concrete, masonry, steel, and wood structures to increase strength and durability.

KEY BENEFITS

  • Fast wet-out of fiberglass reinforcements with minimal drainage from lamination
  • Greater fatigue resistance, strength and reinforcement
  • Flexible carbon fiber wrap conforms to any shape
  • Less weight and lower thermal expansion
  • Reduced installation time
  • Infrastructure seismic upgardes (concrete beams, columns, pipes)
  • Carbon fiber or glass filiment winding (pressure tanks, vessels)
  • Fatigue resistant FRP manufactured parts
  • Composite tooling
  • Blast Mitigation
  • Construction Equipment
  • Bridges and piers
  • Fuel tank sealers
Allow the composite to cure at the recommended temperature as listed in the physical properties chart (above). In the case of all listed hardeners, allow at least 6-8 hours at ambient (>65°F) or 2-3 hours at 130°F before attempting to return the composite to service. In colder weather (less than 65°F) allow additional time for the composite to cure.

After the recommended elevated temperature cure, all systems may be exposed to the listed service temperatures. In all cases, an elevated temperature cure of 2-4 hours at 120°F – 140°F assures the highest quality end product.

Liquid and cured physical properties of 1310T with Rhino hardeners:

 RHINO 1310T Composite Resin with:Hardeners
 3102 3103 3138 3191 3136R-1
 Viscosity, cps 3460 2360 2460 2900 2500
 Parts Hardener by Weight 22 22 22 43 20
 Mix Ratio by Volume 4:1 4:1 4:1 2:1 5:1
 Gel Time Min (150gr) 12-15 30-35 50-60 60-70 25-30
 HDT, °F 190 190 240 175 265
 Set Time, Hrs @ 77°F 2 4 5 4 3
 Cure Time, Hrs @ 130°F 2 3 4 3-4 3-4
 Shore D Hardness (24 hr room temp cure) 80 78 80 75 85
 Elongation % 4.5 4.5 4.0 5.0 2.5

   All listed hardeners cure very rapidly with the addition of heat, via hot water or hot air at a    temperature of 120˚F-140˚F.

All hardeners reach sufficient strength for return to service or demolding after an overnight ambient cure. The fastest Rhino hardener, Rhino 3102, is useful for winter applications, or for mixing in smaller batches. Rhino 3103 is the standard 30-minute system hardener used for 4:1 volume mixing applications. Rhino 3138 should be used in high temp applications (up to 240˚F) and is 4:1 by volume, which is also useful in hot weather or for large areas. Rhino 3191 is our standard 1 hour General Purpose hardener, and may be certified to NSF Standard 61 for potable water.

Rhino 3136R-1 is used for composite tooling. Rhino hardeners, 3102, 3103 and 3191 are DOT not regulated / DOT non-corrosive, minimizing hazardous materials shipping issues.

Rhino 1310T resin post cured at 130°F for 4 hours with all listed hardeners. For reference purposes only, these properties are measured as a composite using A-260 unidirectional e-glass, glass to resin ratio of 60:40.

 Property Result Test Method
 Tensile Strength (psi) >30,000 ASTM D-638
 Flexural Strength (psi) >32,000 ASTM D-790
 Compressive Strength (psi) >20,000 ASTM D-695
 Izod Impact Strength (ft/lb/in) >40 ASTM D-256A
 Heat Deflection Temp >170°F RHINO
>0
TENSILE STRENGTH (PSI)
>0
FLEXURAL STRENGTH (PSI)
>0
COMPRESSIVE STRENGTH (PSI)
0º
HEAT DEFLECTION TEMP (°F)

APPLICATION PROCESS